Surface topography evolution of Ni-based single crystal superalloy under laser shock: Formation of the nano-scale surface reliefs
论文编号:
第一作者: Lu, GX;Liu JD(刘纪德);Qiao HC(乔红超);Zhou YZ(周亦胄);Jin T(金涛);Sun XF(孙晓峰);Hu ZQ(胡壮麒)
联系作者:
发表年度: 2017
期: 3
卷: 123
页: 1-10
摘要: The aim of the study was to investigate the effect of laser shock peening (LSP) on surface topography evolution of metallic targets. Samples manufactured by a Ni-based single crystal superalloy with polished finish were treated by LSP, and the surface topographies before and after LSP were examined by non-contact White-Light Interferometer (WLI). Results showed the following three aspects: (a) By taking advantage of WLI, the shrinkage porosities and the interdendritic structures were observed simultaneously. (b) With the increasing impact times, the round pit induced by laser shock became deeper. (c) The nano-scale surface reliefs were found on the bottom of round pit induced by LSP, and the specific plastic flow of metallic materials under the action of compressive stresses was deemed as the primary contributor to the formation of surface reliefs. It revealed a novel microscale plastic deformation phenomenon of metallic materials in surface strengthening.
英文摘要:
刊物名称: Applied Physics A: Materials Science and Processing
学科:
论文出处:
论文类别:
参与作者:
影响因子:
全文链接: